Using steps as follows:

(1) Use a soft wool brush for brushing. After each brushing, ignite to dry; confirm that the mould is completely extinguished (blow with compressed air to ensure safety) and then brush again;

(2) Number of brushing: In order to ensure the effect of the coating and prevent the casting from sticking to the sand, the number of brushing should in principle ensure that the thickness of the coating can completely cover the sand mold. After brushing, no sand or pits or gaps between sand particles can be seen on the surface of the sand mold.

This product will not harden. If the adjusted coating is not used up on the same day, cover it, and when it is used again, stir evenly before use.

We supply high quality full mold coating to our customers.

1.  Full mold casting coating  pdf 

Ⅰ. Application：

Suitable for cast iron and cast steel parts.

Ⅱ. Advantages：

1.Has good suspension and fast drying, can be naturally dried in the air or through 50 ℃-55℃drying, on-site easy to use.

2.Add special resin reinforcing agent, so that the total white mold adhesive strength is high the appearance has a good rigidity , to solve the problem of casting deformation after the coating dry strength is high ,no moisture ,no cracking ,no delamination ,significantly improve the casting yield .

3.Has good hanging and leveling property and good air permeability , good anti-sand property , easy to clean the castings.

Ⅰ. Application

Suitable for cast iron, cast steel and non-ferrous alloy.

Ⅱ. Product advantages

1.The composite aggregate with excellent fire resistance determines the

good anti-sticking and metal penetration properties of the coating.

2 .In brushing, the thixotropy of the coating causes it to liquefy, spread,

adhere to the surface of the core, and penetrate a certain depth;

3 .Excellent thixotropy and suspension stability

4.Excellent flow coating properties, evenly smooth coating after flow

coating, no flow marks, no traces.

Ⅰ. Application: Suitable for cast iron, cast steel and non-ferrous alloys.

Ⅱ. Advantages: 1. Good adhesion, high strength after drying or self-drying, no delamination, no cracking, etc.

2. It has good stability under high temperature impact

3. Good peeling performance, small air volume, smooth casting surface, no sticky sand